My prints get very good adhesion to the bed, especially when doing prints with large adhesion areas. So good, that after the print is done, I actually have to wet the surface with alcohol and put it in the freezer for it to let go! (edit: I print with PLA)

My question is, if the adhesion could be a bit less violent, if I lower or increase the bed temperature? I have an ender 3 v2 with the original glass bed (it has some black layer on top of the glass).

I know that there are tons of alternative beds that I could buy, but I’d rather keep this bed if I can counter the too strong adhesion

    • HewlettHackardEnglish
      3·
      11 months ago

      Yup. My kid found the idea hilarious when I explained why I’d swiped a washable glue stick from the arts and crafts box.

      It hangs on well, but also makes removal easier.

    • kensand@sopuli.xyzEnglish
      2·
      11 months ago

      I use the washable gluesticks for my polycarbonate prints. I just put PC prints under warm water for a few minutes and they pop right off. Gluesticks generally reduce bed adhesion though IME, so it’s a fine line to walk; I never use gluesticks with PETG for example because then the parts don’t stick to the bed enough.

    • rambos@lemm.eeEnglish
      2·
      11 months ago

      Adhesion can be better, but it also acts as a release agent. If you are printing PETG on glass always use glue, for PLA it shouldnt be needed.

        • rambos@lemm.eeEnglish
          2·
          11 months ago

          In my experience PLA just pops off the clean glass when cooled to room temp (holds extremely well if bed is at 45C or more). I have some tips, but only to improve adhesion xD You can maybe try less squish on the first layer (lower flow rate or increase nozzle distance a bit) or just use thin layer of glue. Too low or too high bed temp can ruin bed adhesion, but feels like wrong approach imo, still worth a try